| Two-component isolating sealant for glasses |
 |
| silicone |
 |
SP-1020
It is characterized by high subsequent duratility and elasticity. The Hardening material possesses excellent adhesion to glass, aluminum and steel. Probably automatic drawing.
|
 |
Technical characteristics
Base: Polysulphidic sealing Putty
Color:
Basis (component A) white
The hardener (component B) Black
Density: 1600kgs / cubic meter
Proportion of components of a gas mixture on weight (The relation of concentration of components of mix on weight.)
Weight rate of A:B: 10:1
Temperature of Application: 15 –
35 Centigrade
Ambient temperature: - 40 C to 80 C
Spreadable life: (Depending on Humidity and thickness): 0.5 –
1.5 hour
Hardness shore: A
Strength of Coupling abruption ( After hardening during 72 hours under standard climate conditions.)
Material: Aluminum alloy 0.8Mpa
Glass silicate: 0.8Mpa
Percentage elongation on the moment of break: 100-200%
Relative residual deformation after break: 30%
Vapour permeability: 5.2r/m2/24 hour
Package: 280kgs for Component A
28kgs for component B
shelf life: 6 Months on dry place at 15 –
25 Centigrade
|