| Elastuff 160 |
 |
Primerless polyurethane coating
ELASTUFF 160 is a two-component, 100% solids polyurethane coating system. This unique thermosetting rubber is especially formulated to achieve exceptional adhesion to properly prepared metal surfaces without the need of a separate primer coat. ELASTUFF 160develops a dense, high durometer finish due to the nature of its highly crosslinked polymer. This slick, non-porous surface provides excellent release properties, which also contributes to its resistance to abrasion and tearing. ELASTUFF 160 has a tenacious bond to Near White or White Metal blasted surface, as well as primed concrete, primed wood and polyurethane foam. Where ultimate cathodic disbondment protection is required, this polyurethane coating system is available as ELASTUFF 160 CD. The CD (cathodic disbondment) package extends ELASTUFF 160use to buried pipe, tank and supports.
ELASTUFF 160 provides outstanding protection on surfaces subject to abrasion in either dry or aqueous solutions or environments. Due to the excellent hydrophobicity of ELASTUFF 160 it is extremely effective as a tank or pipe lining subjected to fresh water, salt water and slurry solutions as well as a wide range of fuels, oils and other hydrocarbons, waste/water containment, interior pipe, exterior buried pipe and tanks, underground metal structures, hoppers, chutes and dumpers. ELASTUFF 160can also be applied over concrete surfaces where a slick, dense finish is desired to aid in release or flow characteristics. It is equally effective in providing abrasion and impact resistance over polyurethane foam. ELASTUFF 160can also be applied as a liner for potable water movement and storage. It is non-toxic and meets the potable water tank lining requirements outlined in A.W.W.A. Standards. Both ELASTUFF 160and ELASTUFF 160CDare fast, thermosetting polyurethane and are designed exclusively for use with 1:1 ration plural component spray application equipment. High vertical hold gives ELASTUFF 160 the ability to uniformly cover weld seams, bolts, angles and edges as well as other irregular surfaces. |
 |
Mixing Ratio: 1 Part A to 1 Part B by volume (1A:1B)
Flash Point: Part A > 200'F (93'C) , Part B > 200'F (93'C)(Seta-Flash closed cup)
Dry Time to Touch:2 to 3 hours @ 75'F, 50% R.H.(can be boosted)
Cure Time: 80% after 24 hours @ 75'F, 50% R.H.
Water Absorption: Less than 1% weight gain after 7 days
Tensile Strength:2500 psi (¡¾100)
Elongation:30% (¡¾10)
Tear Strength:250 lbs/inch (¡¾30)
Hardness:70-80 Shore D @ 75'F, 50% R.H.
Abrasion Resistance:65-75 mg weight loss with H-10 wheels using 1000gm weights at 1000 revolutions
Pot Life: 2 to 3 minutes @ 75'F, 50% R.H. |
|
|
|
 |
|
|
|
|
|
 |