| PAXON BA7794 |
 |
| Polyethylene |
 |
| High Density Polyethylene |
 |
BA7794 is a 25% talc-filled, high molecular weight, high density polyethylene.
This color matchable material has been specifically developed as a cost effective resin for applications requiring excellent stiffness, impact and heat deflection temperatures.
Its design features include excellent rigidity, dimensional stability, warpage resistance, and heat deflection temperature.
It also has good low temperature impact resistance.
Resin must be dried just prior to the blow molding or sheet extrusion process.
* Applications:
-Automotive seat backs
-Automotive dunnage trays
-Automotive load floors
-Refrigerator liners
-Ice chests
-Other recreational applications |
 |
Type: IV
Class: A
Category: 5
Melt Index, 190/2.16 (g/10 min): <0.1
Flow Rate, 190/21.6 (HLMI) (g/10 min): 11.3
Density lbs/ft(g/cm): 71.1(1.14)
Tensile Strength at Yield psi (MPa): 4,100 (28)
Tensile Strength at Break psi (MPa): 1,700 (12)
Elongation at Yield (%): 7
Elongation at Break (%): 20
Flexural Modulus psi (MPa): 380,000(2,620)
Tensile Impact ft-lbs/in(joules/cm): 45 ( 9.5)
Gardner Impact in-lbs(joules) 350 (40) |
|
|
|
 |
|
|
|
|
|
 |