| ACHIEVE 1635E1 |
 |
| Propylene Polymer |
 |
Low haze, premium injection molding propylene homopolymer resin based on Exxpol metallocene technology.
Provides higher HDT and flexural modulus than conventional HPP and much lower extractable content and lower haze.
Especially useful for fast cycle injection molding of a variety of clear articles including thin-walled rigid packaging and products. |
 |
Melt Flow Rate (230'C/2.16 kg): 28.5 g/10 min
Density: 0.90 g/cm 3
DSC Melting Temperature: 152 ¡ÆC
Molecular Weight Distribution: Narrow
Haze on 40 mil plaque: 8-10 %
Tensile Strength @ Yield (2 in/min, 50 mm/min): 5.2 kpsi 36 MPa
Elongation @ Yield (2 in/min, 50 mm/min): 7 %
Flexural Modulus, 1% Secant (0.05 in/min, 1.3 mm/min): 230 kpsi 1590 MPa
Izod Impact Strength Notched, @ 23'C (73'F): 0.5 ft-lb/in 27 J/m
Mold Shrinkage: 1.3 %
Heat Deflection Temperature @ 66 psi, 455 kPa: 241'F 116'C |
|
|
|
 |
|
|
|
|
|
 |