| ACHIEVE 1605 |
 |
| propylene homopolymer |
 |
Premium injection molding propylene homopolymer resin based on Exxpol metallocene technology.
Provides higher HDT and flexural modulus than conventional homopolymers and much lower extractable content. |
 |
Melt Flow Rate (230'C/2.16 kg): 32 g/10 min
Density: 0.90 g/cm 3
DSC Melting Temperature: 149'C
Molecular Weight Distribution: Narrow
Tensile Strength @ Yield(2 in/min, 50 mm/min): 4.6 kpsi 32 MPa
Elongation @ Yield (2 in/min, 50 mm/min): 9 %
Flexural Modulus, 1% Secant (0.05 in/min, 1.3 mm/min): 180 kpsi 1240 MPa
Izod Impact Strength Notched, @ 23'C (73'F): 0.4 ft-lb/in 22 J/m
Heat Deflection Temperature @ 66 psi, 455 kPa: 201'F 94'C |
|
|
|
 |
|
|
|
|
|
 |