| EXXONMOBIL PD9505 E1 |
 |
| Copolymer |
 |
| Exceptionally clear, high melt flow rate polymer of propylene and ethylene specifically designed for injection-stretch blow molding of high clarity bottles and injection molding of clear articles, where good organoleptic properties are required. |
 |
Melt Flow Rate (230'C/2.16 kg): 30 g/10 min
Haze (0.04 in injection molded plaque): 8 %
Tensile Strength @ Yield (2 in/min, 50 mm/min): 4.3 kpsi 30 MPa
Tensile Strength @ Break (2 in/min, 50 mm/min): 2.3 kpsi 16MPa
Elongation @ Yield (2 in/min, 50 mm/min): 21 %
Elongation @ Break (2 in/min, 50 mm/min): 410 %
Flexural Modulus, 1% Secant (0.05 in/min, 1.3 mm/min): 160 kpsi 1100 MPa
Gardner Impact 0.125 in (3.175 mm) thick disk @ 23'C (73'F): 221 in-lb 25 J |
|
|
|
 |
|
|
|
|
|
 |